Effect of Different Ratio of Eu$211$ Phase on the Superconducting Properties of EuBCO Bulk Superconductor

8P-03
Jul 10, 2025, 5:30 PM
1h 30m
POSTER Topic 8 - Strongly correlated electron systems, superconducting materials POSTER Session

Speaker

Dr Liudmila Vojtkova (Institute of Experimental Physics, Slovak Academy of Sciences)

Description

Bulk single crystals of EuBCO superconductors with different Eu$211$ phase contents were prepared. Higher growth rates in the growth temperature window than usual were used to grow bulk EuBCO crystals, and the Eu$211$ phase content in the samples was varied from $21.7$ to $32.2$ wt.$\%$.

Measurements of local superconducting properties (transition temperature, critical current density at $77$ K) and macroscopic superconducting properties (trapped magnetic field and levitation force at $77$ K) of the prepared materials were performed. The microstructure of the samples was studied by polarized light microscopy and scanning electron microscopy. The influence of different Eu$211$ phase contents, growth rates, resulting sizes and volume fraction distributions of Y$211$ particles on the measured superconducting properties was shown.

Acknowledgment

This work was supported by Slovak Grant Agency APVV-17-0625, APVV-21-0387, VEGA 2/0094/22. The work was created at the Institute of Experimental Physics of the SAS as part of the project solution SAS Return Project Scheme 2025.

Primary author

Dr Liudmila Vojtkova (Institute of Experimental Physics, Slovak Academy of Sciences)

Co-authors

Dr Pavel Diko (Institute of Experimental Physics SAS Slovak Academy of Sciences) Dr Michal Rajňák (Institute of Experimental Physics, Slovak Academy of Sciences)

Presentation materials

There are no materials yet.